| Pwojè | Alfa-1924 | Metòd eksperyans |
| Aparans | Likid klè ak transparan san koulè ak jòn limyè | Enspeksyon vizyèl |
| Dansite (20 degre), g / cm3 | 0.855 | ASTM D1298 |
| Viskozite sinematik, mm2/s | ASTM D445 | |
| 100 degre | 4 | |
| 40 degre | 16 | |
| Endèks viskozite | 156 | ASTM D2270 |
| Flash point (ouvèti), degre | 242 | ASTM D92 |
| Vide pwen, degre | -37 | ASTM D97 |
| Valè asid, mgKOH / g | 0.03 | ASTM D974 |
| Pèt evaporasyon Noyak (250 degre, 1h), % | 4.2 | ASTM D5800 |
| Low temperature dynamic viscosity@-35 degree , mPa.s | 1100 | ASTM D5293 |
| Koyefisyan friksyon | 0.1167 | UTM* |
| pwen anilin, degre | 60 | ASTM D611 |
| Kondiktivite tèmik (50 degre), W/mK | 0.19 | ASTM E1461 |
| Chalè espesifik (50 degre), J/gK | 2.76 | ASTM E1269 |
| Kondiktif (20 degre), ns/m | 1.89 | DIN EN 60247 |
| Pann vòltaj, KV | 40 | ASTM D877 |